Nanostructured Ball-Milled Ni–Co–Mn Oxides from Spent Li-Ion Batteries as Electrocatalysts for Oxygen Evolution Reaction

FalihahBalqis,YuyunIrmawati,DongshengGeng,FerryAnggoroArdyNugroho,AfriyantiSumboja
ACS Applied Nano Materials Pub Date : 07/20/2023 00:00:00 , DOI:10.1021/acsanm.3c02092
Abstract
Discovering sources of transition metals, such as Ni, Co, and Mn, has become crucial due to their broad applicability, particularly as electrocatalysts for the oxygen evolution reaction (OER). Upcycled spent batteries have emerged as alternatives for transition metal sources for the OER electrocatalysts. In this work, Ni–Co–Mn oxalates were extracted from the spent LiNixCoyMnzO2 (NCM) cathode of lithium-ion batteries. The extracted oxalates were further processed via ball milling as a rapid and scalable mechanochemical route to engineer their structures. After calcination, Ni–Co–Mn oxides with nanosized granules on the surface that mainly consist of MnCo2O4 were obtained. With a correlation of morphology and trimetallic oxide formation with the OER catalytic performance, Ni–Co–Mn oxides exhibit OER overpotentials of 367 and 732 mV in alkaline and neutral media, respectively, showing OER catalytic activity in a wide pH range. The results indicate that ball milling can induce particle size reduction and bond formation between metals to facilitate mixed-metal oxide formation. Furthermore, the resulting material is also applicable as the catalyst in the air cathode of Zn-air batteries, where the battery achieved a power density of 85.42 mW cm–2 and 100 h of cycling stability, showing comparability with a battery with a Pt/C–Ir/C catalyst.
引用文献
推荐文献
微信二维码
  • 微信公众号二维码
  • 关注官方微信公众号
  • 微信二维码
  • 微信扫码联系客服
平台客服